FAQ
Answer 3 - Can I specify a thicker coating than normal and if so, will I achieve a correspondingly increased lifespan from my steel?
Current indications are that the normal coating thickness of 85 microns will protect most articles for well in excess of 40 years. Therefore, increasing the coating thickness is not necessary except in extreme circumstances. However, should it be required there are two ways it can be achieved:
a) by surface roughening;
b) by using reactive steels. Both of these methods will increase the zinc pick-up and extend the life to first maintenance accordingly.
Surface Roughening:
Grit-blast the surface to Sa2 using chilled angular iron grit of size G24. This roughens and increases the surface area of steel in contact with molten zinc and leads to an increase in the weight per unit area of a hot dip galvanised coating by up to 50%.
Reactive Steels:
A thicker zinc coating can be achieved if the article to be galvanised is manufactured from a reactive steel.
The constituents in steel that have the greatest influence on the iron/zinc reaction are silicon and phosphorous. When an article is removed from the galvanising bath, a pure zinc layer adheres to the alloy layer. The reaction rate in these steels can be so high that this zinc layer is transformed completely to zinc-iron alloy before the article has time to cool.
The result is a coating of equal or increased thickness which can be much duller in appearance than normal. We recommend that you consult with us prior to specifying an increased coating to confirm that the desired result can be achieved. It also allows us to monitor the steel before and during the galvanising to ensure compliance.
Questions
Question 1 :
We have a large balcony project and the Architect has requested that it be painted after Hot Dip Galvanising. We have heard that most paint will not adhere directly to freshly galvanised steel. Is this true and how should we overcome this problem?
Question 2 :
How long does it take to galvanise steel?
Question 4 :
We recently had to carry out some remedial work on site, prior to erecting a Hot Dip Galvanised steel structure. The architect on the job was concerned that we might have intrinsically damaged the corrosion protection of the steel. Is this the case ?Answer