Answers 4 -We recently had to carry out some remedial work on site, prior to erecting a Hot Dip Galvanised steel structure. The architect on the job was concerned that we might have intrinsically damaged the corrosion protection of the steel. Is this the case ?

Small areas of galvanising may be damaged by operations such
as cutting or welding. Also, small areas of damage may occur in transport and erection.

Because of the sacrificial action of zinc, localised flaws (up to 5mm in diameter) tend to be self healing and have little effect on the life of thecoating.

Nevertheless, it is often aesthetically desirable to renew the coating over small areas as well as larger areas using one of the following techniques.

a) Thoroughly wire-brush the affected areas and apply several coats of zinc-rich primer (min. 90% zinc content) to give a coating thickness at least equivalent to the original galvanising.

Many of these paints deposit zinc at about 150g/m/coat; This will usually give a dull coating as illustrated. A top coat of of 'bright galvanising spray' may be then applied to achieve a suitable colour match Areas of galvanising which are damaged - for instance by welding - may be readily made good. Here system (a) above has been used.

b) Thoroughly wire-brush then heat the bare area with a blow torch to 300°C and apply special zinc alloy rod;

c) Grit-blast the affected area to Sa3 and zinc spray. A 100µm sprayed coating confers corrosion protection equivalent to an 85µm galvanised coating. Painting with zinc-rich paint is usually the simplest method but if a colour match is important, then zinc alloy rods are more suitable.

IS EN/ISO 1461 gives guidance on all matters such as coating thicknessand renovation procedures as well as size of areas acceptable for treatment. Areas of galvanising which are damaged - for instance by welding - may be readily made good. Here zinc dust paint has been used.

Questions

Question 1 :

We have a large balcony project and the Architect has requested that it be painted after Hot Dip Galvanising. We have heard that most paint will not adhere directly to freshly galvanised steel. Is this true and how should we overcome this problem?

Answer

Question 2 :

How long does it take to galvanise steel?

Answer

Question 3 :

Can I specify a thicker coating than normal and if so, will I achieve a correspondingly increased lifespan from my steel?

Answer